Effects of Coagent Functionalities on Properties of Ultrafine Fully Vulcanized Powdered Natural Rubber Prepared as Toughening Filler in Rigid PVC
Open Access
- 18 January 2021
- Vol. 13 (2), 289
- https://doi.org/10.3390/polym13020289
Abstract
Ultrafine fully vulcanized powdered natural rubber (UFPNR) has a promising application as a renewable toughening modifier in polymer matrices. In this work, the effects of acrylate coagents, which had different amounts of functional groups, on properties of UFPNR produced by radiation vulcanization and spray-drying was systematically investigated for the first time. Dipropylene glycol diacrylate (DPGDA), trimethylol propane trimethaacrylate (TMPTMA), and ditrimethylol propane tetraacrylate (DTMPTA) were used as coagents with two, three, and four acrylate groups, respectively. The radiation in the range of 250 to 400 kGy and coagent contents of up to 11 phr were used in the production process. Physical, chemical, and thermal properties of the UFPNR were characterized by swelling analysis, scanning electron microscopy, infrared spectroscopy, thermogravimetric analysis, and differential scanning calorimetry. The properties of UFPNR produced by using different type and content of coagents were compared and discussed. The results revealed that UFPNR with the smallest particle size of 3.6 ± 1.1 μm and the highest thermal stability (Td5 = 349 °C) could be obtained by using DTMPTA, which had the highest amount of functional group. It was proposed that the coagent with the greater number of acrylate groups enhanced the crosslinking of natural rubber as it had more reactive groups. Finally, an application of UFPNR as a toughening filler in rigid PVC was demonstrated with 34% improvement of impact strength.Keywords
Funding Information
- National Research Council of Thailand (xxx)
- National Science and Technology Development Agency (xxx)
This publication has 31 references indexed in Scilit:
- Enhancing viscoelastic and mechanical performances of natural rubber through variation of large and small rubber particle combinationsPolymer Testing, 2020
- Advances in toughened polymer materials by structured rubber particlesProgress in Polymer Science, 2019
- Composite properties of graphene-based materials/natural rubber vulcanized using electron beam irradiationMaterials Today Communications, 2019
- Viscoelastic and mechanical properties of large- and small-particle natural rubber before and after vulcanizationPolymer Testing, 2018
- Enhancing mechanical properties of prevulcanized natural rubber latex via hybrid radiation and peroxidation vulcanizations at various irradiation dosesRadiation Effects and Defects in Solids, 2018
- Effect of gamma irradiation on properties of ultrafine rubbers as toughening filler in polybenzoxazineRadiation Physics and Chemistry, 2018
- High performance natural rubber composites with a hierarchical reinforcement structure of carbon nanotube modified natural fibersMaterials & Design (1980-2015), 2014
- Radiation vulcanization of natural rubber with polyfunctional monomersPolymer Bulletin, 2013
- Thermal properties and crystallization behavior of ultrafine fully‐vulcanized powdered rubber particle toughened polypropyleneJournal of Applied Polymer Science, 2008
- Novel Rubber Blends Made from Ultra-Fine Full-Vulcanized Powdered Rubber (UFPR)Polymer Journal, 2006