Elasto-Plastic Fracture Mechanics Analysis of the Effect of Shot Peening on 300M Steel
Open Access
- 25 June 2021
- Vol. 14 (13), 3538
- https://doi.org/10.3390/ma14133538
Abstract
A modified J-integral calculation method is adopted to fix the problem of the quantitative evaluation of the crack propagation of shot-peened structures. Considering the residual stress, residual strain, and residual strain energy, the effect of shot peening on the J-integral parameters of semi-elliptic surface crack fronts is quantitatively calculated and a method is provided for the performance evaluation of the shot peening layer. First, the shot peening process is simulated, then the fatigue crack is generated by changing the constraint condition and a far-field load is applied to calculate the J-integral parameters, crack propagation rate, and crack kinking angle. The effects of different crack depths and shot velocities on the fracture parameters are analyzed. The results show that the reduction in the J-integral value after shot peening decreases with the increase in the crack depth when the shot velocity is a certain value, which indicates that shot peening is more beneficial for suppressing the fatigue crack propagation. When the crack depth is greater than the depth of the compressive stress layer, shot peening accelerates the crack propagation. The reduction in the J-integral value decreases with the increase in shot velocity when the crack depth is a certain value; therefore, increasing shot velocity is more beneficial for retarding fatigue crack propagation.Keywords
This publication has 23 references indexed in Scilit:
- Effect of shot peening intensity on surface integrity of 18CrNiMo7-6 steelSurface and Coatings Technology, 2021
- Effect of pneumatic shot peening on the high and low cycle combined fatigue life of K403 turbine bladesFatigue & Fracture of Engineering Materials & Structures, 2021
- Optimization of the Duration of Ultrasonic Shot Peening for Enhancement of Fatigue Life of the Alloy Ti-6Al-4VJournal of Materials Engineering and Performance, 2020
- Effect of shot peening on short crack propagation in 300M steelInternational Journal of Fatigue, 2019
- Influence of micro arc oxidation coating thickness and prior shot peening on the fatigue behavior of 6061-T6 Al alloyInternational Journal of Fatigue, 2019
- Microstructural characterisation of metallic shot peened and laser shock peened Ti–6Al–4VActa Materialia, 2017
- Weight function for circumferential semi-elliptical cracks in cylinders due to residual stress fields induced by weldingArchive of Applied Mechanics, 2015
- Numerical study on fatigue crack growth in railway wheels under the influence of residual stressesEngineering Failure Analysis, 2015
- Progresses on Research and Application of Metal Ultrasonic Surface Enhancement TechnologiesJournal of Mechanical Engineering, 2014
- Experimental investigation and fatigue life prediction for 7475-T7351 aluminum alloy with and without shot peening-induced residual stressesActa Materialia, 2011