Synthesis and characterization of novel polyimides based on 10,10-bis[4-(4-aminophenoxy)-3-methylphenyl]-9(10H)-anthrone
- 1 June 2020
- journal article
- research article
- Published by Informa UK Limited in Journal of Macromolecular Science, Part A
- Vol. 57 (10), 734-742
- https://doi.org/10.1080/10601325.2020.1770100
Abstract
10,10-Bis[4-(4-aminophenoxy)-3-methylphenyl]-9(10H)-anthrone, as a novel aromatic diamine, was synthesized from anthrone by three-step process. A series of polyimides containing methyl substituents and 9(10H)-anthrone pendant groups was prepared from this diamine with various aromatic dianhydrides via the poly(amic acid) (PAA) precursors and subsequent thermal or chemical imidization procedure. Inherent viscosities of PAAs are between 0.87 and 1.58 dL/g, and the corresponding polyimides have the weight-average molecular weight and number-average molecular weight in the range of 49,400–64,200 and 28,700–37,700, respectively. Most of the polyimides obtained through the chemical cyclodehydration method are soluble in NMP, DMF, DMAc, Py and m-cresol at room temperature. These polyimides have glass transition temperatures of 289–313 °C, 10% weight loss temperatures of 484–524 °C, char yields of 55–63% at 800 °C, and temperature at the maximum-rate degradation of 560–584 °C in nitrogen, respectively. The polyimide films obtained through the thermal imidization have tensile strength of 76.43–119.74 MPa, elongation at break of 6.93–12.33%, and tensile modulus of 1.91–2.38 GPa.Keywords
This publication has 29 references indexed in Scilit:
- Organosoluble, low-dielectric-constant fluorinated polyimides based on 9,9-bis[4-(4-amino-2-trifluoromethyl- phenoxy)phenyl]xanthenePolymer International, 2011
- High-performance aromatic polyamidesProgress in Polymer Science, 2010
- Synthesis and characterization of some aromatic polyimidesJournal of Applied Polymer Science, 2009
- Synthesis and properties of organosoluble polyimides derived from bis(4‐amino‐3,5‐dimethyl phenyl) halo phenyl methane and various dianhydridesJournal of Applied Polymer Science, 2006
- Synthesis and characterization of new highly organosoluble poly(ether imide)s based on 3,3?,5,5?-tetramethyl-2,2-bis[4-(4-dicarboxyphenoxy)phenyl]propane dianhydrideJournal of Polymer Science Part A: Polymer Chemistry, 2002
- Synthesis and properties of new soluble poly(amide-imide)s from 3,3′,5,5′-tetramethyl-2,2-bis[4-(4-trimellitimidophenoxy)phenyl]propane with various diaminesPolymer, 1999
- Synthesis and properties of new adamantane-based poly(ether imide)sJournal of Polymer Science Part A: Polymer Chemistry, 1999
- Syntheses and properties of organosoluble polyamides and polyimides based on the diamine 3,3-bis[4-(4-aminophenoxy)-3-methylphenyl]phthalide derived fromo-cresolphthaleinJournal of Polymer Science Part A: Polymer Chemistry, 1999
- Syntheses and properties of aromatic polyamides and polyimides derived from 9,9‐bis[4‐(p‐aminophenoxy)phenyl]fluoreneJournal of Polymer Science Part A: Polymer Chemistry, 1993
- Cardo PolymersJournal of Macromolecular Science, Part C: Polymer Reviews, 1974