Significant Conductivity Enhancement of Conductive Poly(3,4-ethylenedioxythiophene): Poly(styrenesulfonate) Films through a Treatment with Organic Carboxylic Acids and Inorganic Acids
- 2 February 2010
- journal article
- research article
- Published by American Chemical Society (ACS) in ACS Applied Materials & Interfaces
- Vol. 2 (2), 474-483
- https://doi.org/10.1021/am900708x
Abstract
Significant conductivity enhancement was observed on transparent and conductive poly(3,4-ethylene dioxythiophene):poly(styrene sulfonate) (PEDOT:PSS) films after a treatment with organic and inorganic acids, including acetic acid, propionic acid, butyric acid, oxalic acid, sulfurous acid, and hydrochloric acid. The conductivity could be enhanced from 0.2 to over 200 S cm−1, that is, by a factor of more than 1000. The conductivity enhancement was dependent on the structure of the acids and the experimental conditions during the treatment, such as the acid concentration and the temperature. The optimal temperature was in the range of 120 to 160 °C. The resistance dropped rapidly when a PEDOT:PSS film was treated with acid solution of high concentration, whereas it gradually increased and then decreased when it was treated with an acid solution of low concentration. The mechanism for this conductivity enhancement was studied by various chemical and physical characterizations. The temperature dependence of conductivity indicates that the energy barrier for charge hopping among the PEDOT chains become lower in the highly conductive PEDOT:PSS film after the acid treatment. The ultraviolet−visible−near-infrared (UV−vis−NIR) absorption spectroscopy, the X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (SEM) indicate the loss of polystyrene sulfonic acid (PSSH) chains from the PEDOT:PSS film after the acid treatment, and the atomic force microscopy (AFM) suggest conformational change of the polymer chains. Therefore, the conductivity enhancement is attributed to the loss of PSSH chains from the PEDOT:PSS film and the conformational change of the PEDOT chains, which are induced by the acids.Keywords
This publication has 35 references indexed in Scilit:
- Salt-Induced Charge Screening and Significant Conductivity Enhancement of Conducting Poly(3,4-ethylenedioxythiophene):Poly(styrenesulfonate)Macromolecules, 2009
- Significant Conductivity Enhancement of Conductive Poly(3,4-ethylenedioxythiophene):Poly(styrenesulfonate) Films by Adding Anionic Surfactants into Polymer SolutionMacromolecules, 2008
- A Morphological Model for the Solvent‐Enhanced Conductivity of PEDOT:PSS Thin FilmsAdvanced Functional Materials, 2008
- Influence of Ionic Liquids on the Electrical Conductivity and Morphology of PEDOT:PSS FilmsChemistry of Materials, 2007
- On the mechanism of conductivity enhancement in poly(3,4-ethylenedioxythiophene):poly(styrene sulfonate) film through solvent treatmentPolymer, 2004
- Conductivity, morphology, interfacial chemistry, and stability of poly(3,4‐ethylene dioxythiophene)–poly(styrene sulfonate): A photoelectron spectroscopy studyJournal of Polymer Science Part B: Polymer Physics, 2003
- Molecular organic light-emitting diodes using highly conducting polymers as anodesApplied Physics Letters, 2002
- Enhancement of electrical conductivity of poly(3,4-ethylenedioxythiophene)/poly(4-styrenesulfonate) by a change of solventsSynthetic Metals, 2001
- Processible Optically Transparent Block Copolymer Films Containing Superparamagnetic Iron Oxide NanoclustersChemistry of Materials, 1997
- Two doping structures and structural anisotropy revealed by the mass loss and shrinkage of polypyrrole films on alkali treatmentSynthetic Metals, 1995