The effect of the silica content of silica fume on its ability to control alkali–silica reaction
- 1 August 2003
- journal article
- Published by Elsevier in Cement and Concrete Research
- Vol. 33 (8), 1263-1268
- https://doi.org/10.1016/s0008-8846(03)00058-9
Abstract
No abstract availableKeywords
This publication has 8 references indexed in Scilit:
- Use of the Accelerated Mortar Bar Test for Evaluating the Efficacy of Mineral Admixtures for Controlling Expansion due to Alkali-Silica ReactionCement, Concrete and Aggregates, 1999
- Why the Accelerated Mortar Bar Method ASTM C 1260 is Reliable for Evaluating the Effectiveness of Supplementary Cementing Materials in Suppressing Expansion Due to Alkali-Silica ReactivityCement, Concrete and Aggregates, 1995
- Application of the NaOH bath test method for assessing the effectiveness of mineral admixtures against reaction of alkali with artificial siliceous aggregateCement and Concrete Composites, 1994
- The effectiveness of supplementary cementing materials in suppressing expansion due to ASR: Another look at the reaction mechanisms part 1: Concrete expansion and portlandite depletionCement and Concrete Research, 1994
- Evaluation of the validity of the pore solution expression method from hardened cement pastes and mortarsCement and Concrete Research, 1994
- The effectiveness of supplementary cementing materials in suppressing expansion due to ASR: Another look at the reaction mechanisms part 2: Pore solution chemistryCement and Concrete Research, 1994
- Alkali-silica reaction: The relation between pore solution characteristics and expansion test resultsCement and Concrete Research, 1990
- Expression and analysis of pore fluids from hardened cement pastes and mortarsCement and Concrete Research, 1981