The influence of thermal treatment on the chemistry and structure of grain boundaries in inconel 600
- 1 August 1981
- journal article
- Published by Springer Nature in Metallurgical Transactions A
- Vol. 12 (8), 1397-1408
- https://doi.org/10.1007/bf02643684
Abstract
No abstract availableKeywords
This publication has 30 references indexed in Scilit:
- Relationship Between Acid Intergranular Corrosion and Caustic Stress Corrosion Cracking of Alloy 600Corrosion, 1977
- Stress Corrosion Cracking of Stainless Steel and Nickel Alloys at Controlled Potentials in 10% Caustic Soda Solutions at 550°FJournal of the Electrochemical Society, 1976
- Intergranular stress-assisted corrosion cracking of austenitic alloys in water-cooled nuclear reactorsJournal of Nuclear Materials, 1975
- Further observations on the effect of grain boundary segregation in the hydrogen embrittlement of nickelMetallurgical Transactions A, 1975
- The intergranular embrittlement of nickel by hydrogen: The effect of grain boundary segregationMetallurgical Transactions, 1974
- Stress Corrosion Cracking of Iron and Nickel Base Alloys in Sulfate Solutions at 289 CCorrosion, 1973
- Discussion of Chemistry of Grain Boundaries and Its Relation to Intergranular Corrosion of Austenitic Stainless Steel(1)Corrosion, 1973
- Carbide Sensitization and Intergranular Corrosloe of Nickel Base AlloysCorrosion, 1971
- Übersicht der elektkrochemischen Methoden zur Untersuchung von Wasserstoffversprödung und SpannungrsrißkorrosionMaterials and Corrosion, 1970
- The influence of hydrogen on the plastic deformation ductility, and fracture of nickel in tensionActa Metallurgica, 1963