Fatigue crack propagation behavior of a single crystalline superalloy
- 1 August 1990
- journal article
- Published by Springer Nature in Metallurgical Transactions A
- Vol. 21 (8), 2169-2177
- https://doi.org/10.1007/bf02647878
Abstract
No abstract availableKeywords
This publication has 29 references indexed in Scilit:
- Fatigue crack propagation in Ni-base superalloy single crystals under multiaxial cyclic loadsMetallurgical Transactions A, 1986
- Stress intensity factors for anisotropic compact-tension specimens with inclined cracksEngineering Fracture Mechanics, 1986
- Crack growth in a single crystal superalloy at elevated temperatureMetallurgical Transactions A, 1984
- Crack tip plasticity and crack growth in a single-crystal superalloy at elevated temperaturesMaterials Science and Engineering, 1984
- Gamma prime shape changes during creep of a nickel-base superalloyScripta Metallurgica, 1983
- Effects of load ratio and temperature on the near-threshold fatigue crack propagation behavior in a CrMoV steelMetallurgical Transactions A, 1983
- Application of the Electrical Potential Method to Crack Length Measurements Using Johnson's FormulaJournal of Testing and Evaluation, 1981
- Analysis of crystallographic high temperature fatigue crack growth in a nickel base alloyMetallurgical Transactions A, 1981
- INCORPORATING THRESHOLD AND ENVIRONMENTAL EFFECTS INTO THE DAMAGE ACCUMULATION MODEL FOR FATIGUE CRACK GROWTHFatigue & Fracture of Engineering Materials & Structures, 1980
- Crack-morphological aspects in fracture mechanicsEngineering Fracture Mechanics, 1975