An analysis of reported fatigue crack growth rate data with special reference to Ti-6A1-4V
- 31 December 1977
- journal article
- Published by Elsevier in Engineering Fracture Mechanics
- Vol. 9 (2), 509-520
- https://doi.org/10.1016/0013-7944(77)90042-x
Abstract
No abstract availableKeywords
This publication has 17 references indexed in Scilit:
- The influence of crystallographic orientation on fatigue crack growth in strongly textured Ti6A14VActa Metallurgica, 1975
- Observations of an interface phase in the α/β boundaries in titanium alloysMetallurgical Transactions A, 1975
- Fatigue crack propagation in austenitic stainless steelsEngineering Fracture Mechanics, 1975
- A review of fatigue crack growth in high strength aluminum alloys and the relevant metallurgical factorsEngineering Fracture Mechanics, 1973
- Fatigue crack growth retardation after single-cycle peak overload in Ti-6Al-4V titanium alloyEngineering Fracture Mechanics, 1973
- Fatigue crack propagation in martensitic and austenitic steelsMetallurgical Transactions, 1973
- Mechanisms of fatigue crack growth in low alloy steelActa Metallurgica, 1973
- The role of fracture toughness in low-cycle fatigue crack propagation for high-strength alloysEngineering Fracture Mechanics, 1973
- The influence of stress intensity and microstructure on fatigue crack propagation in ferritic materialsEngineering Fracture Mechanics, 1972
- Numerical Analysis of Crack Propagation in Cyclic-Loaded StructuresJournal of Basic Engineering, 1967