The stacking-fault energy in the Ag-In series
- 1 October 1966
- journal article
- research article
- Published by Informa UK Limited in Philosophical Magazine
- Vol. 14 (131), 971-978
- https://doi.org/10.1080/14786436608244768
Abstract
The intrinsic stacking-fault energy has been determined in the Ag-In series using extended nodes, from pure silver to Ag-12.5 wt. % In (e/a = 1.23). The present results show that the stacking-fault energy is insensitive to alloying up to e/a ≁ 1.04, after which it decreases with increasing solute content. Extrinsic faulting has been observed throughout the alloy series including pure silver and in all cases the extrinsic and intrinsic stackingfault energies are approximately equal. Following high temperature annealing treatments, the effective stacking-fault energy in high solute content alloys is observed to increase irreversibly, suggesting the presence of a solute impedance force at room temperature.Keywords
This publication has 18 references indexed in Scilit:
- Stacking-Fault Energy of a Ag-In Alloy from Node MeasurementsJournal of Applied Physics, 1966
- Extended Dislocation Nodes in a Silver-Tin AlloyJournal of Applied Physics, 1966
- An Absolute Determination of the Extrinsic and Intrinsic Stacking Fault Energies in Ag-In AlloysPhysica Status Solidi (b), 1966
- On the determination of stacking fault energies from extended dislocation node measurementsActa Metallurgica, 1965
- The self-stress of dislocations and the shape of extended nodesPhilosophical Magazine, 1964
- X-Ray Diffraction Study of the Effects of Solutes on the Occurrence of Stacking Faults in Silver-Base AlloysJournal of Applied Physics, 1962
- Stacking Fault Energy in SiliconJournal of Applied Physics, 1962
- Diffraction contrast of electron microscope images of crystal lattice defects. III. Results and experimental confirmation of the dynamical theory of dislocation image contrastProceedings of the Royal Society of London. Series A. Mathematical and Physical Sciences, 1962
- Direct measurements of stacking-fault energies from observations of dislocation nodesPhilosophical Magazine, 1961
- Single crystal elastic constants of silver and silver alloysActa Metallurgica, 1956