Spherical‐Impact Damage and Strength Degradation in Silicon Carbide Whisker/Silicon Nitride Composites
- 1 May 1989
- journal article
- Published by Wiley in Journal of the American Ceramic Society
- Vol. 72 (5), 791-798
- https://doi.org/10.1111/j.1151-2916.1989.tb06219.x
Abstract
No abstract availableKeywords
This publication has 29 references indexed in Scilit:
- Impact Fracture of Chemically Tempered Glass Helicopter WindshieldsJournal of the American Ceramic Society, 1986
- Erosion of a Silicon Carbide Whisker Reinforced Silicon NitrideMRS Proceedings, 1986
- Impact Fracture of Thermally Tempered Glass Helicopter WindshieldsJournal of the American Ceramic Society, 1985
- Fracture Toughness Predictions for Crack Bowing in Brittle Particulate CompositesJournal of the American Ceramic Society, 1983
- Double‐Cantilever‐Beam Testing of a Transversely Isotropic Fibrous Silica MaterialJournal of the American Ceramic Society, 1983
- Comparisons of Static and Impact Loading Damage in Zinc SulfideJournal of the American Ceramic Society, 1982
- Mechanisms of Toughening in Ceramic Matrix CompositesCeramic Engineering and Science Proceedings, 1981
- Equilibrium penny-like cracks in indentation fractureJournal of Materials Science, 1975
- Strength Degradation of Brittle Surfaces: Blunt IndentersJournal of the American Ceramic Society, 1975
- Strength Degradation by Projectile ImpactsJournal of the American Ceramic Society, 1973