X-Ray Peak Profiles for Ultramicrotomed Powders and Their Relation to the Deformation Structure
- 1 July 1968
- journal article
- research article
- Published by AIP Publishing in Journal of Applied Physics
- Vol. 39 (8), 3587-3592
- https://doi.org/10.1063/1.1656829
Abstract
X‐ray peak profiles of microtomed powders have been measured. The results for peak shifts and for peak asymmetries have been related to observations by transmission electron microscopy. The validity of the assumptions that have been made to calculate the relationship between peak profiles and stacking faults or twin faults is discussed.Keywords
This publication has 14 references indexed in Scilit:
- Deformation of Some fcc Metals by UltramicrotomyJournal of Applied Physics, 1968
- X-Ray Measurements of Faulting in α Cu-Ge AlloysJournal of Applied Physics, 1964
- Single- and Double-Deformation Faults in Face-Centered Cubic CrystalsJournal of Applied Physics, 1963
- Diffraction by face-centered cubic crystals containing extrinsic stacking faultsActa Crystallographica, 1963
- Determination of Twin Fault Probabilities from the Diffraction Patterns of fcc Metals and AlloysJournal of Applied Physics, 1962
- Lattice Parameter Studies of Annealed, of Aged, and of Cold-Worked Alpha BrassJournal of Applied Physics, 1962
- The influence of grain size on deformation stacking faults in brass filingsActa Metallurgica, 1961
- Stacking Fault Probability of Noble Metal-Zinc AlloysJournal of Applied Physics, 1961
- X-ray studies of deformed metalsProgress in Metal Physics, 1959
- X-Ray Diffraction by Face-Centered Cubic Crystals with Deformation FaultsJournal of Applied Physics, 1952