Recovery and recrystallization of the deformed, orderable alloy (Co78Fe22)3V

Abstract

An alloy of composition (Co₇₈Fe₂₂)₃V, which orders to an L1₂ superlattice below a critical temperature (T_c) of 910 °C, was rolled to 25–50% reduction in the initially ordered condition and annealed at various temperatures above and below T_c and examined by hardness, tensile testing, optical and electron microscopy and dilatometry, in order to study the progress of recovery and recrystallization. Recrystallization was severely retarded on annealing below T_c; close to T_c, recrystallization was ≈ 300 × slower in the ordered than the disordered range. Although recrystallization started promptly, predominantly at grain boundaries, very rapid recovery-softening of the unrecrystallized regions progressively reduced the driving force for recrystallization and slowed it down drastically. However, at 770°and 500 °C, recovery-softening was replaced by some recovery-hardening (i.e., strain-age hardening). Above T_c, recrystallization was complete in a few seconds and a special annealing method was needed to measure such times accurately. Dilatometric measurements showed that most of the order destroyed by rolling was restored long before recrystallization began, but the restoration was never complete unless the alloy was heated up through T_c and then slow cooled. Electron microscopy showed no sign of any antiphase domains in recrystallized grains except for a few isolated domain boundaries on annealing at 770 °C. A model is proposed to rationalize the incidence of recovery-softening or strain-age hardening at different annealing temperatures.