Graphitized Pitch-Based Carbons with Ordered Nanopores Synthesized by Using Colloidal Crystals as Templates
Top Cited Papers
- 1 March 2005
- journal article
- research article
- Published by American Chemical Society (ACS) in Journal of the American Chemical Society
- Vol. 127 (12), 4188-4189
- https://doi.org/10.1021/ja0423466
Abstract
A highly graphitized ordered nanoporous carbon (ONC) was synthesized by using commercial mesophase pitch as carbon precursor and siliceous colloidal crystal as template. Since silica colloids of different sizes (above 6 nm) and narrow particle size distribution are commercially available, the pore size tailoring in the resulting ONCs is possible.Keywords
This publication has 25 references indexed in Scilit:
- A Simple Melt Impregnation Method to Synthesize Ordered Mesoporous Carbon and Carbon Nanofiber Bundles with Graphitized Structure from PitchesThe Journal of Physical Chemistry B, 2004
- Synthesis of Polyacrylonitrile-Based Ordered Mesoporous Carbon with Tunable Pore StructuresChemistry of Materials, 2003
- Orthogonal Carbon Nanofibers by Template-Mediated Assembly of Discotic Mesophase PitchAdvanced Materials, 2003
- Formation of Ordered Mesoporous Carbon Material from a Silica Template by a One-Step Chemical Vapour Infiltration ProcessChemistry Letters, 2002
- High surface area graphitized carbon with uniform mesopores synthesised by a colloidal imprinting methodElectronic supplementary information (ESI) available: experimental: preparation of the graphitized colloid-impregnated carbon. See http://www.rsc.org/suppdata/cc/b2/b200702a/Chemical Communications, 2002
- Fabrication of wellordered macroporous active carbon with a microporous frameworkJournal of Materials Chemistry, 2001
- Synthesis of New, Nanoporous Carbon with Hexagonally Ordered MesostructureJournal of the American Chemical Society, 2000
- Synthesis of Highly Ordered Carbon Molecular Sieves via Template-Mediated Structural TransformationThe Journal of Physical Chemistry B, 1999
- Carbon Structures with Three-Dimensional Periodicity at Optical WavelengthsScience, 1998
- Effect of Micropore Topology on the Structure and Properties of Zeolite Polymer ReplicasChemistry of Materials, 1997