DIRECT EXPERIMENTAL EVIDENCE OF DISLOCATIONS
- 1 January 1959
- journal article
- research article
- Published by SAGE Publications in Metallurgical Reviews
- Vol. 4 (1), 101-140
- https://doi.org/10.1179/095066059790421773
Abstract
When a metal crystal is deformed plastically, the crystal changes its shape by the slipping of atomic planes over one another. In this process the atomic planes do not slip over each other as rigid entities; instead, slip starts at one or more places in the slip plane and then spreads gradually over the remainder of the plane. In general, therefore, there will be a boundary line on the slip plane dividing the area over which slip has already taken place from that over which slip has not yet occurred. This boundary line between the slipped and unslipped parts ot the crystal is a dislocation line. A dislocation is essentially a line defect; in the neighbourhood of the dislocation the atoms are displaced from their positions in the ideally perfect crystal lattice.Keywords
This publication has 26 references indexed in Scilit:
- Dislocation Etch Pit Formation in Lithium FluorideJournal of Applied Physics, 1958
- Evidence of Dislocation Jogs in Deformed SiliconJournal of Applied Physics, 1958
- Arrangements of Dislocations in Plastically Bent Silicon CrystalsJournal of Applied Physics, 1958
- Dislocation Arrays in GermaniumJournal of Applied Physics, 1957
- Observations on the dislocation structure of germanium crystalsActa Metallurgica, 1957
- Dislocations in plastically indented GermaniumActa Metallurgica, 1957
- Copper Precipitation on Dislocations in SiliconJournal of Applied Physics, 1956
- Observations of Dislocation Glide and Climb in Lithium Fluoride CrystalsJournal of Applied Physics, 1956
- Dislocations in GermaniumJournal of Applied Physics, 1955
- Interfacial Free Energy of Coherent Twin Boundaries in CopperJournal of Applied Physics, 1951