Stage III recovery in electron-irradiated platinum
- 1 January 1969
- journal article
- research article
- Published by Taylor & Francis in Radiation Effects
- Vol. 1 (1), 65-67
- https://doi.org/10.1080/00337576908234461
Abstract
The dominant high temperature recovery peak in irradiated platinum is observed between 500 °K and 700 °K, dependent on dose. Pre-quenched irradiated platinum shows an additional peak at higher temperatures. Stage III in platinum is relabelled stage II.Keywords