Highly Ordered Anodic Porous Alumina with 13‐nm Hole Intervals Using a 2D Array of Monodisperse Nanoparticles As a Template
- 1 March 2006
- Vol. 2 (4), 522-525
- https://doi.org/10.1002/smll.200500440
Abstract
No abstract availableKeywords
This publication has 15 references indexed in Scilit:
- Ideally ordered anodic porous alumina with Sub-50nm hole intervals based on imprinting using metal moldsJournal of Vacuum Science & Technology B: Microelectronics and Nanometer Structures, 2005
- Fabrication of Highly Ordered Anodic Porous Alumina Using Self-organized Polystyrene Particle ArrayChemistry Letters, 2004
- Synthesis of Highly Crystalline and Monodisperse Maghemite Nanocrystallites without a Size-Selection ProcessJournal of the American Chemical Society, 2001
- Fabrication of ideally ordered anodic porous alumina with 63 nm hole periodicity using sulfuric acidJournal of Vacuum Science & Technology B: Microelectronics and Nanometer Structures, 2001
- Highly ordered nanochannel-array architecture in anodic aluminaApplied Physics Letters, 1997
- Block Copolymer Lithography: Periodic Arrays of ~10 11 Holes in 1 Square CentimeterScience, 1997
- Fabrication of Gold Nanodot Array Using Anodic Porous Alumina as an Evaporation MaskJapanese Journal of Applied Physics, 1996
- Ordered Metal Nanohole Arrays Made by a Two-Step Replication of Honeycomb Structures of Anodic AluminaScience, 1995
- Fabrication and Magnetic Properties of Arrays of Metallic NanowiresScience, 1993
- Nanochannel Array GlassScience, 1992