Role of Potassium Acetate Deicer in Accelerating Alkali–Silica Reaction in Concrete Pavements
- 1 January 2011
- journal article
- Published by SAGE Publications in Transportation Research Record: Journal of the Transportation Research Board
- Vol. 2240 (1), 70-79
- https://doi.org/10.3141/2240-10
Abstract
About 15 years after the introduction of alkali–acetate and alkali–formate deicers, premature deterioration was observed on some airfield pavements that had been exposed to the deicers. A characteristic map cracking pattern was observed on pavement surfaces that had experienced repeated applications of these deicers, and the suspected cause of this cracking pattern was accelerated alkali–silica reaction (ASR). Laboratory-based research indicated that alkali–silica reactive aggregates may undergo active deterioration when intimately exposed to such deicers under conditions promoting accelerated reaction. Investigations were conducted on cores collected from an airport whose deicing operations involved repeated applications of potassium acetate deicer. Detailed microscopic investigation indicated that uniform distress existed throughout the depth of the pavement, although in one, the distress resulted from alkali-carbonate reaction rather than from ASR. However, investigations on the depth of penetration of deicer into these pavement cores showed only limited incursion. A companion laboratory study estimated the extent of deicer penetration under different laboratory exposure conditions. Even in a relatively aggressive wetting and drying exposure regime, ingress of the deicer was limited. Thus, it was concluded that although the potassium acetate deicer can induce severe ASR under aggressive laboratory conditions, penetration into field airport pavements may be so limited in some cases that the potassium acetate deicer does not seem to aggravate the ASR distress should one already exist.Keywords
This publication has 9 references indexed in Scilit:
- Influence of acetate and formate-based deicers on ASR in airfield concrete pavementsCement and Concrete Research, 2010
- Modified ASTM C 1293 Test Method to Investigate Potential of Potassium Acetate Deicer Solution to Cause Alkali-Silica ReactionTransportation Research Record: Journal of the Transportation Research Board, 2007
- Damaging effects of deicing chemicals on concrete materialsCement and Concrete Composites, 2006
- Investigation into Potential of Alkali-Acetate-Based Deicers to Cause Alkali-Silica Reaction in ConcreteTransportation Research Record: Journal of the Transportation Research Board, 2006
- Laboratory and field investigations of the influence of sodium chloride on alkali–silica reactivityCement and Concrete Research, 2003
- Testing Concrete for AAR in NaOH and NaCl solutions at 38°C and 80°CCement and Concrete Composites, 1994
- Characteristics of alkali-silica reaction in the presence of sodium and calcium chlorideCement and Concrete Research, 1990
- Studies of alkali-silica reaction. Part 4. Effect of different alkali salt solutions on expansionCement and Concrete Research, 1987
- Studies of alkali-silica reaction. Part 3. Mechanisms by which NaCl and Ca(OH)2 affect the reactionCement and Concrete Research, 1986