Room-temperature intermediate layer bonding for microfluidic devices
- 12 October 2009
- journal article
- Published by Royal Society of Chemistry (RSC) in Lab on a Chip
- Vol. 9 (24), 3481-3488
- https://doi.org/10.1039/b914270c
Abstract
In this work a novel room-temperature bonding technique based on chemically activated Fluorinated Ethylene Propylene (FEP) sheet as an intermediate between chemically activated substrates is presented. Surfaces of silicon and glass substrates are chemically modified with APTES bearing amine terminal groups, while FEP sheet surfaces are treated to form carboxyl groups and subsequently activated by means of EDC–NHS chemistry. The activation procedures of silicon, glass and FEP sheet are characterized by contact angle measurements and XPS. Robust bonds are created at room-temperature by simply pressing two amine-terminated substrates together with activated FEP sheet in between. Average tensile strengths of 5.9 MPa and 5.2 MPa are achieved for silicon–silicon and glass–glass bonds, respectively, and the average fluidic pressure that can be operated is 10.2 bar. Moreover, it is demonstrated that FEP-bonded microfluidic chips can handle mild organic solvents at elevated pressures without leakage problems. This versatile room-temperature intermediate layer bonding technique has a high potential for bonding, packaging, and assembly of various (bio-) chemical microfluidic systems and MEMS devices.Keywords
This publication has 47 references indexed in Scilit:
- Atmospheric-pressure plasma pretreatment for direct bonding of silicon wafers at low temperaturesSurface and Coatings Technology, 2008
- UV surface exposure for low temperature hydrophilic silicon direct bondingMicrosystem Technologies, 2008
- Room temperature SiO2∕SiO2 covalent bondingApplied Physics Letters, 2006
- Room temperature wafer level glass/glass bondingSensors and Actuators A: Physical, 2005
- Fluorine-enhanced low-temperature wafer bonding of native-oxide covered Si wafersApplied Physics Letters, 2004
- Room temperature bonding of micromachined glass devices for capillary electrophoresisSensors and Actuators B: Chemical, 2000
- Formation of Silicon Structures by Plasma-Activated Wafer BondingJournal of the Electrochemical Society, 2000
- Low-temperature direct bonding of silicon and silicon dioxide by the surface activation methodSensors and Actuators A: Physical, 1998
- Low temperature Si3N4 direct bondingApplied Physics Letters, 1993
- Field Assisted Glass-Metal SealingJournal of Applied Physics, 1969