HIGH FIELD CHARACTERISTICS OF Nb3(Al, Ge)
- 15 July 1968
- journal article
- research article
- Published by AIP Publishing in Applied Physics Letters
- Vol. 13 (2), 68-71
- https://doi.org/10.1063/1.1652511
Abstract
The Jc vs H curve for Nb3(Al0.8Ge0.2) was measured and compared with that of the binary compound Nb3Al. The Nb–Al–Ge alloy curve had a ``peak'' and its resistive critical magnetic field, Hr(J = 0), was above 220 kG at 4.2°K. The composition of the ternary alloy was determined and found to be closer to the ideal 3:1 atomic ratio than that of the binary alloy.Keywords
This publication has 7 references indexed in Scilit:
- Peak Effect in Superconducting Nb-15 at.% Zr-45 at.% Ti AlloysJournal of Applied Physics, 1967
- Superconducting Critical Currents of V3Ga Wires Made by a New Diffusion ProcessJapanese Journal of Applied Physics, 1967
- Superconductivity at 20 Degrees KelvinScience, 1967
- Processing of V3Ga Wires and Their Superconducting PropertiesJapanese Journal of Applied Physics, 1966
- MEASUREMENTS ON NIOBIUM-TIN SAMPLES IN 200-kG CONTINUOUS FIELDSApplied Physics Letters, 1965
- The Peak Effect in Substitutional and Interstitial Solid Solutions of High-Field SuperconductorsReviews of Modern Physics, 1964
- Superconductivity at High Magnetic FieldsPhysical Review B, 1963