Time Decrease of Initial Permeability in MnxFe3−xO4+y
- 1 May 1960
- journal article
- research article
- Published by AIP Publishing in Journal of Applied Physics
- Vol. 31 (5), S267-S268
- https://doi.org/10.1063/1.1984692
Abstract
The time decrease of initial permeability has been measured for several stoichiometric and nonstoichiometric compositions of . The samples were in the form of polycrystalline toroids with compositions , 0.7, 0.85, and 0.9. The stoichiometric compositions, , were fired to maintain a metaloxygen ratio of 3:4, while the nonstoichiometric samples were fired to produce the maximum vacancy concentration. The permeabilities were measured at a peak driving field of 0.002 oe in the temperature range −15° to +35°C. The time decrease data was described by three relaxation times. Activation energies calculated on the basis of these relaxation times were within experimental error equal and independent of the Mn/Fe ratio, i.e., . The activation energy for the nonstoichiometric samples was equal to that observed for the stoichiometric samples. The magnitude of the effect in the stoichiometric samples was found to decrease approximately linearly with the increasing Mn/Fe ratio.
Keywords
This publication has 5 references indexed in Scilit:
- Relation between disaccomodation and magnetic properties of manganese-ferrous ferritePhysica, 1958
- Time Decrease of Permeability in IronJournal of Applied Physics, 1958
- Théorie du traînage magnétique de diffusionJournal de Physique et le Radium, 1952
- Théorie du traînage magnétique des substances massives dans le domaine de RayleighJournal de Physique et le Radium, 1950
- Time effects in magnetizationPhysica, 1938