Natural Cellulose Fibers: Heterogeneous Acetylation Kinetics and Biodegradation Behavior
- 13 April 2001
- journal article
- research article
- Published by American Chemical Society (ACS) in Biomacromolecules
- Vol. 2 (2), 476-482
- https://doi.org/10.1021/bm0056409
Abstract
Steam-exploded fibers from flax (Linum usitatissimum) are heterogeneously acetylated using acetic anhydride and sulfuric acid as catalyst, with the aim to modify the surface properties without changing fiber structure and morphology. The acetylation reaction follows first-order kinetics up to a reaction time that depends on catalyst concentration (15 h when using 0.4 vol % of H2SO4 or 50 h with 0.1 vol %). The fibers undergo no structural and/or morphological changes under either reaction condition. On the contrary, surface damage and structural modifications appear after longer reaction times, when the reaction kinetics change. The extent of biodegradation of acetylated fibers, evaluated from the weight percent remaining after 13 days of exposure to previously isolated cellulolytic bacteria Cellvibrio sp., decreases with increasing acetylation degree. After biodegradation the fibers show a higher acetyl content than before the experiment, indicating that the bacteria preferentially biodegrade unsubstituted cellulose, though also acetylated chains are cleaved. Biodegradable acetylated cellulose fibers with modified surface chemistry and unchanged structure are obtained for applications as polymer composite reinforcements.Keywords
This publication has 27 references indexed in Scilit:
- Preparation, characterization and biodegradation studies on cellulose acetates with varying degrees of substitutionPolymer, 1997
- Properties and modification methods for vegetable fibers for natural fiber compositesJournal of Applied Polymer Science, 1996
- An Infrared Spectroscopic Study of Chemically Modified Chemithermomechanical PulpJournal of Wood Chemistry and Technology, 1993
- Aerobic biodegradation of cellulose acetateJournal of Applied Polymer Science, 1993
- Surface energy of untreated and surface‐modified cellulose fibersJournal of Applied Polymer Science, 1988
- Surface modification of cellulose fibers. I. Spectroscopic characterization of surface‐modified cellulose fibers and their copolymerization with styreneJournal of Applied Polymer Science, 1985
- Three-Dimensional Crystalline Structure of Cellulose Triacetate IIMacromolecules, 1978
- Electronmicroscopic Observations on the Degradation of Cellulose Fibres by Cellvibrio fulvus and Sporocytophaga myxococcoidesJournal of Applied Bacteriology, 1972
- Infrared spectra of cellulose and related polysaccharidesJournal of Polymer Science, 1961
- Infrared spectra of crystalline polysaccharides. II. Native celluloses in the region from 640 to 1700 cm.−1Journal of Polymer Science, 1959