Increases in electrical resistivity after quenching thin bars of uranium monocarbide have been measured and interpreted in terms of lattice vacancies. The activation energy for vacancy formation is deduced as ∼2.8 ev. From annealing experiments the activation energy for movement was found to be ∼1.1 ev and a vacancy makes 5 × 1010−1011 jumps during its lifetime.