Young's modulus and internal friction of graphite irradiated at low temperature
- 1 December 1971
- journal article
- research article
- Published by Taylor & Francis in Radiation Effects
- Vol. 11 (3-4), 155-165
- https://doi.org/10.1080/00337577108231101
Abstract
Samples of pyrolytic graphite and nuclear graphite have been irradiated at 27 or 77 K with neutrons and electrons. The dynamic Young's modulus has been studied by an isochronal annealing method and the internal friction has been measured as a function of temperature. The modulus changes with irradiation dose and annealings have been interpreted using a model based on the pinning of basal dislocations by interstitial atoms. The anneals have revealed an additional effect which was attributed to bonds between interstitial defects and atoms in the adjacent graphite layers. The observed modulus annealing stages are consistent with results of several authors. The internal friction data obtained after low temperature irradiation have been compared with those following room temperature irradiation. Three internal friction peaks have been observed again with activation energies of 0.24, 0.28 and 0.9 eV and interpreted by relaxation processes of interstitial defects. Another peak, at room temperature, has been analysed in terms of interaction between dislocations and point defects. Des irradiations à 27 ou 77 K aux électrons et aux neutrons ont été effectuées sur des échantillons de pyrographite recristallisé et de graphite nucléaire. La gutérison a été étudiée soit par recuits isochrones du module ďYoung dynamique, soit par frottement intérieur en montées linétaires de température. Les évolutions du module avec la dose et les recuits ultérieurs sont décrits par un modèle ďancrage des dislocations basales. Un effet additionnel est mis en évidence après recuit; il est attribué à la formation de couplages entre plans. Les stades de gutérison du module coincident avec ceux observés par ďautres méthodes. Les résultats de frottement intérieur, après irradiation à basse température, sont comparés à ceux obtenus après irradiation à température ambiante. Les spectres de frottement intérieur préentent trois pics dont les énergies ďactivation sont 0,24, 0,28 et 0,9 eV et qui sont interprétis par la relaxation de défauts interstitiels. Un autre pic apparaissant à température ambiante est commenté en termes ďintéraction dislocations-défauts ponctuels.Keywords
This publication has 25 references indexed in Scilit:
- Interstitial atom energies in graphiteCarbon, 1969
- Recovery of the basal plane electrical resistivity in electron-irradiated pyrolytic graphiteCarbon, 1968
- Irradiations du graphite a basse temperature aux neutrons et aux electrons. Mesure de l'energie emmagasinee et des variations de resistivite electriqueCarbon, 1968
- The effect of short-term neutron irradiation on the shear compliance of hot-worked pyrolytic graphiteCarbon, 1968
- Some effects of irradiation at 77°K on the physical properties of graphitePhilosophical Magazine, 1967
- Deformation of graphite lattices by interstitial carbon atomsCarbon, 1966
- The annealing of thermal conductivity changes in electron-irradiated graphitePhilosophical Magazine, 1963
- On the Energy of the Interstitial Atom in GraphiteJournal of the Physics Society Japan, 1961
- The annealing of electron irradiation damage in graphitePhilosophical Magazine, 1960
- Irradiation of Graphite at Liquid Helium TemperaturesPhysical Review B, 1955