Flexibilized Copolyimide Adhesives

Abstract

Two copolyimides, LARC-STPI and STPI-LARC-2, with flexible backbones were prepared and characterized as adhesives. The processability and adhesive properties were compared to those of a commercially available form of LARC-TPI. Lap shear specimens were fabricated using adhesive tape prepared from each of the three polymers. Lap shear tests were performed at room temperature, 177°C, and 204°C before and after exposure to water-boil and to thermal aging at 204°C for up to 1000 hours. The three adhesive systems possess exceptional lap shear strengths at room temperature and elevated temperatures both before and after thermal exposure. LARC-STPI, because of its high glass transition temperature provided high lap shear strengths up to 260°C. After water-boil, LARC-TPI exhibited the highest lap shear strengths at room temperature and 177°C, whereas the LARC-STPI retained a higher percentage of its original strength when tested at 204°C [68% versus 50% (STPI-LARC-2) and 40% (LARC-TPI)]. These flexible thermoplastic copolyimides show considerable potential as adhesives based on this study and because of the ease of preparation with low cost, commercially available materials.