Pure tilt subgrain boundaries in germanium have been studied by high resolution electron microscopy. They contain mainly undissociated edge dislocation and two types of split dislocations. A relatively high intrinsic stacking fault energy is deduced by supposing that no rotation of partials occurs during thinning. No experimental proof has yet been obtained to support this hypothesis