Influence of corrosion deposits on near-threshold fatigue crack growth behavior in 2xxx and 7xxx series aluminum alloys
- 1 December 1982
- journal article
- Published by Springer Nature in Metallurgical Transactions A
- Vol. 13 (12), 2271-2280
- https://doi.org/10.1007/bf02648397
Abstract
No abstract availableThis publication has 23 references indexed in Scilit:
- A geometric model for fatigue crack closure induced by fracture surface roughnessMetallurgical Transactions A, 1982
- Some considerations on fatigue crack closure at near-threshold stress intensities due to fracture surface morphologyMetallurgical Transactions A, 1982
- Oxide-Induced Crack Closure: An Explanation for Near-Threshold Corrosion Fatigue Crack Growth BehaviorMetallurgical Transactions A, 1981
- Oxidation of fatigue fracture surfaces at low crack growth ratesMaterials Science and Engineering, 1980
- INCORPORATING THRESHOLD AND ENVIRONMENTAL EFFECTS INTO THE DAMAGE ACCUMULATION MODEL FOR FATIGUE CRACK GROWTHFatigue & Fracture of Engineering Materials & Structures, 1980
- Near-Threshold Fatigue Crack Growth in 2 1/4 Cr-1Mo Pressure Vessel Steel in Air and HydrogenJournal of Engineering Materials and Technology, 1980
- The influence of environment and stress ratio on fatigue crack growth at near threshold stress intensities in low-alloy steelsEngineering Fracture Mechanics, 1980
- A FATIGUE CRACK CLOSURE MECHANISM IN TITANIUMFatigue & Fracture of Engineering Materials & Structures, 1979
- Fatigue crack growth rates and thresholds in steels under oxidising conditionsMaterials Science and Engineering, 1978
- Threshold Corrosion Fatigue Crack Growth in SteelsJournal of Testing and Evaluation, 1978