Synthesis and Electrochemical Reaction with Lithium of Mesoporous Iron Oxalate Nanoribbons

Abstract

Mesoporous FeC 2O 4 was prepared by dehydration of bulk monoclinic- and micellar orthorhombic FeC 2O 4.2H 2O precursors at 200 degrees C. The micellar material shows nanoribbon shaped particles, which are preserved after dehydration. These solids are used as high-capacity lithium storage materials with improved rate performance. The mesoporous nanoribbons exhibit higher capacities close to 700 mA h/g after 50 cycles at 2C (C = 1 Li h (-1) mol (-1)) rate between 0 and 2 V.