AN ANALYSIS OF CRACK TIP SHIELDING IN ALUMINUM ALLOY 2124: A COMPARISON OF LARGE, SMALL, THROUGH‐THICKNESS AND SURFACE FATIGUE CRACKS
- 1 September 1987
- journal article
- Published by Wiley in Fatigue & Fracture of Engineering Materials & Structures
- Vol. 10 (5), 343-362
- https://doi.org/10.1111/j.1460-2695.1987.tb00485.x
Abstract
No abstract availableKeywords
This publication has 42 references indexed in Scilit:
- On the growth of small fatigue cracks in aluminum-lithium alloy 2090Scripta Metallurgica, 1986
- Short fatigue crack growth behavior in a high strength low alloy steelScripta Metallurgica, 1984
- An empirical stress-intensity factor equation for the surface crackEngineering Fracture Mechanics, 1981
- Elastic-Plastic Analysis of Fatigue Crack Closure in Modes I and IIAIAA Journal, 1980
- The influence of environment and stress ratio on fatigue crack growth at near threshold stress intensities in low-alloy steelsEngineering Fracture Mechanics, 1980
- Dugdale crack closure analysis of fatigue cracks under constant amplitude loadingEngineering Fracture Mechanics, 1979
- Analysis of Closure in Fatigue Crack GrowthJournal of Applied Mechanics, 1978
- Initiation and early growth of fatigue cracks in high strength steelEngineering Fracture Mechanics, 1977
- Cyclic analysis of a propagating crack and its correlation with fatigue crack growthEngineering Fracture Mechanics, 1975
- Fatigue crack closure under cyclic tensionEngineering Fracture Mechanics, 1970