Internal Friction Peaks in Pure Aluminum Observed between 45 and 72°K after α‐Particle Irradiation
- 1 January 1969
- journal article
- research article
- Published by Wiley in Physica Status Solidi (b)
- Vol. 33 (2), 843-850
- https://doi.org/10.1002/pssb.19690330238
Abstract
Relaxation peaks in aluminum found after α‐irradiation at 21.4°K are discussed. In the temperature region of 40 to 75°K, four peaks are observed which anneal out in stage II with first order kinetics. Two of them show the natural line‐width. From the annealing behaviour, the peaks are ascribed to the reorientation of interstitial clusters containing more than two interstitials. The activation energy for reorientation is significantly different from that for annealing.This publication has 5 references indexed in Scilit:
- The clustering of oxygen in solid solution in niobium—II. InterpretationActa Metallurgica, 1966
- Dose dependence of the annealing stage II in neutron irradiated aluminumPhysics Letters, 1966
- Einfluß von α-Bestrahlung bei tiefer Temperatur auf die innere Reibung von hochreinem KupferPhysica Status Solidi (b), 1964
- Analysis of Radiation Annealing Observed during Low Temperature Irradiation with Neutrons and Heavy Charged ParticlesPhysica Status Solidi (b), 1964
- Zwischengitteratome in kubisch-flächenzentrierten kristallen, insbesondere in kupferJournal of Physics and Chemistry of Solids, 1962