Microstructural Changes of Membrane Electrode Assemblies during PEFC Durability Testing at High Humidity Conditions
- 1 January 2005
- journal article
- Published by The Electrochemical Society in Journal of the Electrochemical Society
- Vol. 152 (5), A1011-A1020
- https://doi.org/10.1149/1.1873492
Abstract
Morphological changes occurring in membrane electrode assemblies (MEAs) were monitored using transmission electron microscopy (TEM) during the course of life testing of H2∕airH2∕air polymer electrolyte fuel cells (PEFCs). In the fresh catalyst layers, anode Pt particles were found to have smaller particle sizes, better dispersion, and less agglomeration on the carbon-support surfaces than did the cathode Pt3CrPt3Cr alloy particles. The operation-induced agglomeration of catalyst particles was evaluated for both the anode and cathode after defined life testing periods. Agglomeration of catalyst particles occurred primarily during the first 500 h of testing, which was confirmed by both TEM analysis and electrocatalytic surface area measurement. After 500 h, degradation of the recast Nafion ionomer network within the catalyst layers likely contributes more significantly to MEA performance degradation. Migration of metal catalyst particles toward the interface between the catalyst layer and membrane was observed at both electrodes. The Pt anode catalyst was less stable than the Pt3CrPt3Cr cathode catalyst under high current density and high humidity conditions, which was confirmed by the higher extent of migration observed for the pure Pt than for the Pt3CrPt3Cr . Some Pt particles (from both electrodes) were found to migrate into the membrane during the testing period.Keywords
This publication has 39 references indexed in Scilit:
- Rubbery Graft Copolymer Electrolytes for Solid-State, Thin-Film Lithium BatteriesJournal of the Electrochemical Society, 2005
- Preparation of Cross-Sectional Samples of Proton Exchange Membrane Fuel Cells by Ultramicrotomy for TEMJournal of the Electrochemical Society, 2003
- Determination of Ionic and Electronic Resistivities in Carbon/Polyelectrolyte Fuel-Cell Composite ElectrodesJournal of the Electrochemical Society, 2002
- Nafion content in the catalyst layer of polymer electrolyte fuel cells: effects on structure and performanceElectrochimica Acta, 2001
- Characterization of polymer supported catalysts by cyclic voltammetry and rotating disk voltammetryElectrochimica Acta, 2000
- Performance and endurance of a PEMFC operated with synthetic reformate fuel feedJournal of Power Sources, 1998
- Low platinum loading electrodes for polymer electrolyte fuel cells fabricated using thermoplastic ionomersElectrochimica Acta, 1995
- Effect of sputtered film of platinum on low platinum loading electrodes on electrode kinetics of oxygen reduction in proton exchange membrane fuel cellsElectrochimica Acta, 1993
- The influence of Pt on the electrooxidation behaviour of carbon in phosphoric acidElectrochimica Acta, 1992
- Thin-film catalyst layers for polymer electrolyte fuel cell electrodesJournal of Applied Electrochemistry, 1992