Electro-Spinning and Electro-Blowing of Hyaluronic Acid
- 7 May 2004
- journal article
- research article
- Published by American Chemical Society (ACS) in Biomacromolecules
- Vol. 5 (4), 1428-1436
- https://doi.org/10.1021/bm034539b
Abstract
In this study, hyaluronic acid (HA) was electro-spun and electro-blown to prepare nonwoven nanofibrous membranes. Critical parameters for processing and corresponding effects on the membrane morphology were investigated using the methods of rheology and scanning electron microscopy (SEM). During electro-spinning, the optimal HA concentration window for nanofibrous formation was determined within a narrow range of 1.3−1.5 w/v %, corresponding to a solution viscosity range of 3−30 Pa s at a shear rate of 1 s-1. SEM results indicated that, with increases in (1) the total concentration by blending of low molecular weight HA, (2) the evaporation rate by the addition of ethanol, and/or (3) the feeding rate of solution, the electro-spinning performance for creating nanofibers was improved. However, the improvement was not sufficient to achieve a consistent production of high quality nonwoven nanofiber membranes. This problem was overcome by a new electro-blowing process using the combination of air flow and electro-spinning. Although air blowing at room temperature around the spinneret orifice did not exhibit a remarkable enhancement of nanofiber formation of HA, the performance was significantly improved with an increase in the air blowing rate. SEM results showed that the temperature of air-blowing was the most effective parameter in ensuring HA nanofiber formation. As the temperature of the blown air increased from 25 to 57 °C, the nanofiber formation became consistent and uniform. A high quality HA nonwoven membrane of nanofibers was successfully produced by blowing air at 57 °C with a 70 ft3/hr flow rate.Keywords
This publication has 20 references indexed in Scilit:
- Structure and process relationship of electrospun bioabsorbable nanofiber membranesPolymer, 2002
- Photomediated Solid-State Cross-Linking of an Elastin−Mimetic Recombinant Protein PolymerMacromolecules, 2002
- TAILORING TISSUE ENGINEERING SCAFFOLDS USING ELECTROSTATIC PROCESSING TECHNIQUES: A STUDY OF POLY(GLYCOLIC ACID) ELECTROSPINNINGJournal of Macromolecular Science, Part A, 2001
- Engineered collagen–PEO nanofibers and fabricsJournal of Biomaterials Science, Polymer Edition, 2001
- Concentration Dependence of Interstitial Flow Buffering by Hyaluronan in Synovial JointsMicrovascular Research, 2000
- Processing and microstructural characterization of porous biocompatible protein polymer thin filmsPolymer, 1999
- Synthesis and in Vitro Degradation of New Polyvalent Hydrazide Cross-Linked Hydrogels of Hyaluronic AcidBioconjugate Chemistry, 1997
- DNA fibers by electrospinningJournal of Macromolecular Science, Part B, 1997
- Benign Prostatic HyperplasiaDrugs, 1994
- The Electrical Discharge from Liquid Points, and a Hydrostatic Method of Measuring the Electric Intensity at Their SurfacesPhysical Review B, 1914