Standard enthalpies of formation of some 5d transition metal silicides by high temperature direct synthesis calorimetry
- 23 October 1998
- journal article
- Published by Elsevier in Journal of Alloys and Compounds
- Vol. 280 (1-2), 231-239
- https://doi.org/10.1016/s0925-8388(98)00747-6
Abstract
No abstract availableThis publication has 43 references indexed in Scilit:
- Standard enthalpies of formation of some 4d transition metal silicides by high temperature direct synthesis calorimetryJournal of Alloys and Compounds, 1998
- Standard enthalpies of formation of some 3d transition metal silicides by high temperature direct synthesis calorimetryJournal of Alloys and Compounds, 1998
- Vaporization thermodynamics of the tungsten silicidesJournal of Alloys and Compounds, 1993
- The Disilicides of Tungsten, Molybdenum, Tantalum, Titanium, Cobalt, and Nickel, and Platinum Monosilicide: A Survey of Their Thermodynamic PropertiesJournal of Physical and Chemical Reference Data, 1993
- Ordered intermetallic alloys, part II: Silicides, trialuminides, and othersJOM, 1993
- Thermodynamic properties of silicides I. calorimetric measurements of the specific energy of combustion in fluorine of hyperstoichiometric tungsten disilicide, and the derived standard molar enthalpy of formation ΔfHom(WSi2.060) at the temperature 298.15 KThe Journal of Chemical Thermodynamics, 1992
- Standard enthalpies of formation of Me5Si3 (Me Y, Lu, Zr) and of Hf3Si2Journal of the Less Common Metals, 1990
- Thermodynamics of solid transition-metal silicidesChemical Reviews, 1990
- Thermodynamic Properties of the Tungsten–Silicon and Chromium–Silicon SystemsMetal Science, 1975
- The heats of formation of some transition metal silicidesActa Metallurgica, 1955