Y-Ba-Cu-O Superconducting Films with High Jc Values by MOCVD using Ba-Addition Products
- 1 June 1990
- journal article
- Published by IOP Publishing in Japanese Journal of Applied Physics
- Vol. 29 (6A), L947
- https://doi.org/10.1143/jjap.29.l947
Abstract
Y-Ba-Cu-O superconducting films having high J c of 6.3×106 A/cm2 at 77 K and T c of 92 K were prepared by metalorganic chemical vapor deposition using a new transport technique with Ba-addition products. This CVD method could realize stable vaporization and smooth transportation of Ba source material due to the increase of the evaporation rate at low sublimation temperatures. Consequently, good reproducibility for preparation of the high J c films (over 106 A/cm2) was achieved.Keywords
This publication has 6 references indexed in Scilit:
- Superconducting YBa2Cu3O7−x fibers from the thermoplastic gel methodJournal of Materials Research, 1989
- Preparation of Y-Ba-Cu-O Superconducting Thin Films by the Mist Microwave Plasma Decomposition MethodJapanese Journal of Applied Physics, 1989
- Y-Ba-Cu-O superconducting films prepared on SrTiO3 substrates by chemical vapor depositionApplied Physics Letters, 1988
- Epitaxial ordering of oxide superconductor thin films on (100) SrTiO3 prepared by pulsed laser evaporationApplied Physics Letters, 1987
- Superconducting Y-Ba-Cu-O oxide films by sputteringApplied Physics Letters, 1987
- Thin superconducting oxide filmsPhysical Review B, 1987