A new methodology to investigate fracture toughness of freestanding MEMS and advanced materials in thin film form
- 7 February 2005
- journal article
- Published by Institute of Electrical and Electronics Engineers (IEEE) in Journal of Microelectromechanical Systems
- Vol. 14 (1), 153-159
- https://doi.org/10.1109/jmems.2004.839013
Abstract
This work presents a novel membrane deflection fracture experiment (MDFE) to investigate the fracture toughness of microelectromechanical systems (MEMS) and other advanced materials in thin film form. It involves the stretching of freestanding thin-film membranes, in a fixed-fixed configuration, containing preexisting cracks. The fracture behavior of ultrananocrystalline diamond (UNCD), a material developed at Argonne National Laboratory, is investigated to illustrate the methodology. When the fracture initiates from sharp cracks, produced by indentation, the fracture toughness was found to be 4.5/spl plusmn/0.25 MP m/sup 1/2/. When the fracture initiates from blunt notches with radii about 100 nm, machined by focused ion beam (FIB), the mean value of the apparent fracture toughness was found to be 6.9 MPa m/sup 1/2/. Comparison of these two values, using the model proposed by Drory et al., provides a correction factor of two-thirds, which corresponds to a mean value of /spl rho//2x=1/2.Keywords
This publication has 16 references indexed in Scilit:
- Mechanical Properties of Ultrananocrystalline Diamond Thin Films Relevant to MEMS/NEMS DevicesExperimental Mechanics, 2003
- Fracture strength of polysilicon at stress concentrationsJournal of Microelectromechanical Systems, 2003
- The mechanical strength of polysilicon films: Part 2. Size effects associated with elliptical and circular perforationsJournal of the Mechanics and Physics of Solids, 2003
- A methodology for determining mechanical properties of freestanding thin films and MEMS materialsJournal of the Mechanics and Physics of Solids, 2002
- Fracture toughness of polysilicon MEMS devicesSensors and Actuators A: Physical, 2000
- Fracture of synthetic diamondJournal of Applied Physics, 1995
- Deposition and characterization of nanocrystalline diamond filmsJournal of Vacuum Science & Technology A, 1994
- Fullerenes as precursors for diamond film growth without hydrogen or oxygen additionsApplied Physics Letters, 1994
- Hardness and fracture toughness of semiconducting materials studied by indentation and erosion techniquesMaterials Science and Engineering: A, 1988
- Elastic field equations for blunt cracks with reference to stress corrosion crackingInternational Journal of Fracture, 1967