Small-Angle X-ray Scattering and Rheological Characterization of Alginate Gels. 3. Alginic Acid Gels
- 5 September 2003
- journal article
- research article
- Published by American Chemical Society (ACS) in Biomacromolecules
- Vol. 4 (6), 1661-1668
- https://doi.org/10.1021/bm034105g
Abstract
Alginic acid gels were studied by small-angle X-ray scattering and rheology to elucidate the influence of alginate chemical composition and molecular weight on the gel elasticity and molecular structure. The alginic acid gels were prepared by homogeneous pH reduction throughout the sample. Three alginates with different chemical composition and sequence, and two to three different molecular weights of each sample were examined. Three alginate samples with fractions of guluronic acid residues of 0.39 (LoG), 0.50 (InG), and 0.68 (HiG), covering the range of commercially available alginates, were employed. The excess scattering intensity I of the alginic acid gels was about 1 order of magnitude larger and exhibited a stronger curvature toward low q compared to ionically cross-linked alginate. The I(q) were decomposed into two components by assuming that the alginic acid gel is composed of aggregated multiple junctions and single chains. Time-resolved experiments showed a large increase in the average size of aggregates and their weight fraction within the first 2 h after onset of gelling, which also coincides with the most pronounced rheological changes. At equilibrium, little or no effect of molecular weight was observed, whereas at comparable molecular weights, an increased scattering intensity with increasing content of guluronic acid residues was recorded, probably because of a larger apparent molecular mass of domains. The results suggest a quasi-ordered junction zone is formed in the initial stage, followed by subsequent assembling of such zones, forming domains in the order of 50 Å. The average length of the initial junction zones, being governed by the relative fraction of stabilizing G-blocks and destabilizing alternating (MG) blocks, determines the density of the final random aggregates. Hence, high-G alginates give alginic acid gels of a higher aggregate density compared to domains composed of loosely packed shorter junction zones in InG or LoG system.Keywords
This publication has 10 references indexed in Scilit:
- Small-angle X-ray scattering and rheological characterization of alginate gels. 2. Time-resolved studies on ionotropic gelsJournal of Molecular Structure, 2000
- Small-Angle X-ray Scattering and Rheological Characterization of Alginate Gels. 1. Ca−Alginate GelsMacromolecules, 2000
- Swelling and partial solubilization of alginic acid gel beads in acidic bufferCarbohydrate Polymers, 1996
- Alginic acid gels: the effect of alginate chemical composition and molecular weightCarbohydrate Polymers, 1994
- Alginate as immobilization matrix for cellsTrends in Biotechnology, 1990
- Aspects of the conformation of polyguluronate in the solid state and in solutionInternational Journal of Biological Macromolecules, 1983
- High-field, 1H-n.m.r. spectroscopy of alginate: sequential structure and linkage conformationsCarbohydrate Research, 1983
- Chiroptical and stoichiometric evidence of a specific, primary dimerisation process in alginate gelationCarbohydrate Research, 1978
- Biological interactions between polysaccharides and divalent cations: The egg‐box modelFEBS Letters, 1973
- Scattering by an Inhomogeneous SolidJournal of Applied Physics, 1949