Energies de défaut d'empilement et mécanismes de déformation dans les alliages nickel-chrome

Abstract

STACKING FAULT ENERGIES AND DEFORMATION MECHANISMS IN THE Ni-Cr ALLOYS The study of the f.c.c. Ni-Cr alloys by electron microscopical and tensile deformation techniques shows a reduction of the stacking fault energy from the value for nickel (lower than previously thought) to 75 mJ/m² for 15–40 weight-% chromium. Apparent activation volumes and energies, on the other hand, show continuous decreases with increasing chromium content, although the deformation models based on dislocation intersections and cross slip would suggest larger values when the dissociation of dislocations increases. A similar problem arises in the measurements of Davies, Sagar and Stevens (1973) on Ni-Co alloys. RÉSUMÉ Létude des alliages Ni-Cr c.f.c. par des techniques de microscopic électroniqae et de traction montre que lénergè de défaut d'empilemont tombe de la valour pour le nickel (inférieure aux valeurs antérieurement admises) jusquà 75 mJ/m² pour les alliages à 15–40% do chrome. Les volumes et energies d'activation apparents décroissent par contre continument lorsque la teneur en chrome s'élève, alors que les modèles liant la déformation à des intersections et des déviations de dislocations suggéreraient des valeurs plus élevées quand la dissociation des dislocations grandit. Un problème analogue se pose dans les mesures de Davies et al. (1973) sur les alliages Ni-Co.