Cyclic fatigue-crack propagation along ceramic/metal interfaces
- 30 September 1991
- journal article
- Published by Elsevier in Acta Metallurgica et Materialia
- Vol. 39 (9), 2145-2156
- https://doi.org/10.1016/0956-7151(91)90184-3
Abstract
No abstract availableKeywords
This publication has 17 references indexed in Scilit:
- The strength and fracture of alumina bonded with aluminum alloysActa Metallurgica, 1989
- Cyclic Fatigue Crack Propagation in Alumina under Direct Tension—Compression LoadingJournal of the American Ceramic Society, 1989
- Sandwich test specimens for measuring interface crack toughnessMaterials Science and Engineering: A, 1989
- Ceramic/metal interfacial crack growth: Toughening by controlled microcracks and interfacial geometriesActa Metallurgica, 1988
- Crack Paralleling an Interface Between Dissimilar MaterialsJournal of Applied Mechanics, 1987
- AN ANALYSIS OF CRACK TIP SHIELDING IN ALUMINUM ALLOY 2124: A COMPARISON OF LARGE, SMALL, THROUGH‐THICKNESS AND SURFACE FATIGUE CRACKSFatigue & Fracture of Engineering Materials & Structures, 1987
- Microelectronic PackagingScientific American, 1983
- Stress Corrosion and Static Fatigue of GlassJournal of the American Ceramic Society, 1970
- Discussion: “Edge-Bonded Dissimilar Orthogonal Elastic Wedges Under Normal and Shear Loading” (Bogy, D. B., 1968, ASME J. Appl. Mech., 35, pp. 460–466)Journal of Applied Mechanics, 1969
- Plane Problems of Cracks in Dissimilar MediaJournal of Applied Mechanics, 1965