Structural and optical properties of self-assembled AlN nanowires grown on SiO2/Si substrates by molecular beam epitaxy
- 3 February 2021
- journal article
- research article
- Published by IOP Publishing in Nanotechnology
- Vol. 32 (19), 195601
- https://doi.org/10.1088/1361-6528/abe2c7
Abstract
Self-assembled AlN nanowires (NWs) are grown by plasma-assisted molecular beam epitaxy (PAMBE) on SiO2 / Si (111) substrates. Using a combination of in-situ reflective high energy electron diffraction and ex situ X-ray diffraction (XRD), we show that the NWs grow nearly strain-free, preferentially perpendicular to the amorphous SiO2 interlayer and without epitaxial relationship to Si(111) substrate, as expected. Scanning electron microscopy investigation reveals significant NWs coalescence, which results in their progressively increasing diameter and formation of columnar structures with non-hexagonal cross-section. Making use of scanning transmission electron microscopy (STEM), the NWs initial diameters are found in the 20 – 30 nm range. In addition, the formation of a thin (≈30 nm) polycrystalline AlN layer is observed on the substrate surface. Regarding the structural quality of the AlN NWs, STEM measurements reveal the formation of extended columnar regions, which grow with a virtually perfect metal-polarity wurtzite arrangement and with extended defects only sporadically observed. Combination of STEM and electron energy loss spectroscopy (EELS) reveals the formation of continuous aluminum oxide (1–2 nm) on the NW surface. Low temperature photoluminescence measurements reveal a single near-band-edge (NBE) emission peak, positioned at 6.03 eV (at 2 K), a value consistent with nearly zero NW strain evidenced by XRD and in agreement with the values obtained on AlN bulk layers synthesized by other growth techniques. The significant full-width-at-half-maximum of NBE emission, found at ≈20 meV (at 2 K), suggests that free and bound excitons are mixed together within this single emission band. Finally, the optical properties of the hereby reported AlN nanowires grown by PAMBE are comprehensively compared to optical properties of bulk, epitaxial and/or columnar AlN grown by various techniques such as: physical vapor transport (PVT), metal organic vapor phase epitaxy (MOVPE), metal organic chemical vapor deposition (MOCVD) and molecular beam epitaxy (MBE).Keywords
Funding Information
- Spain’s Ministry of Science and Innovation under Grants (RTI2018-097338-B-100)
This publication has 26 references indexed in Scilit:
- An AlGaN Core–Shell Tunnel Junction Nanowire Light-Emitting Diode Operating in the Ultraviolet-C BandNano Letters, 2017
- Single Photons from a Hot Solid-State Emitter at 350 KACS Photonics, 2016
- Aluminum nitride nanowire light emitting diodes: Breaking the fundamental bottleneck of deep ultraviolet light sourcesScientific Reports, 2015
- Formation Mechanisms of GaN Nanowires Grown by Selective Area Growth HomoepitaxyNano Letters, 2015
- Ultralow-threshold electrically injected AlGaN nanowire ultraviolet lasers on Si operating at low temperatureNature Nanotechnology, 2015
- Advances in group III-nitride-based deep UV light-emitting diode technologySemiconductor Science and Technology, 2010
- GaN Substrates—Progress, Status, and ProspectsIEEE Journal of Selected Topics in Quantum Electronics, 2009
- Ti-mask Selective-Area Growth of GaN by RF-Plasma-Assisted Molecular-Beam Epitaxy for Fabricating Regularly Arranged InGaN/GaN NanocolumnsApplied Physics Express, 2008
- The effect of the III/V ratio and substrate temperature on the morphology and properties of GaN- and AlN-layers grown by molecular beam epitaxy on Si(1 1 1)Journal of Crystal Growth, 1998
- Growth of Self-Organized GaN Nanostructures on Al2O3(0001) by RF-Radical Source Molecular Beam EpitaxyJapanese Journal of Applied Physics, 1997